Product name

Cracking paste    咨詢電話：13713145387陳秋婷   QQ：1747383364

State

Paste

Packing

25KG/drum for white,  20KG/drum for clear

Storage

6 months in cool place

Application

Suitable for knitting

Features

1. High fastness

2. High softness

3. SGS detecting passed, no PVC, no heavy metal, no NPEOs.

Mix proportion

Light: White cracking paste 70-100% + Clear cracking paste 0-30% + pigment ?% + fixing agent 2%

Deep: White cracking paste 20-30% + Clear cracking paste 70-80% + pigment ?% + fixing agent 2%

Printing process

1. Printing with clear cracking paste ( for underbase) for 1-2 times

2. Mixing with white cracking paste, clear cracking paste, pigment, fixing agent and stirring them evenly.

3. Printing again for 2-3 times (3-4 scrapes per time).

4. Drying the paste surface with cold air, it will be cracked by itself after it’s dry.

5. Hot pressing the printing for about 5 seconds with 150℃ to make it better adhesion.

6. Finish. 

Attentions

1. Thick screen is suggested for the best effect (print for 1 time only).  If with thin screen,  please printing for 2-3 times, and blow the paste surface with cold air to dry it fast and re-printing before it’s cracked.

2. Please take the fabric up after it’s completely cracked, otherwise it’s won’t be cracked naturally.

3. More clear and thinner the paste is , thinner the crack is.

4. The pigment can not be exceeded in 12%, otherwise it'll be easily faded. 

品名

特軟龜裂漿          咨詢電話：13713145387陳秋婷  QQ：1747383364

外觀

糊狀

包裝

白膠漿25KG/桶，透明漿20KG/桶，打底透明漿20KG/桶

貯存期

常溫下6個(gè)月

應(yīng)用

針織布

調(diào)配比例

印淺色：龜裂白膠漿70-100% +龜裂透明漿0-30% + 色漿？% + 固化劑2%

印深色：龜裂白膠漿20-30% + 龜裂透明漿70-80% + 色漿？% + 固化劑2%

賣(mài)點(diǎn)

1. 可耐正常水洗

2. 手感柔軟

工藝流程

1. 絲網(wǎng)選用80-100目，用絲印硬方刀75度刮印，先用龜裂打底透明漿打底+固化劑印1-2次,

第一板用力刮4-6刀，

2. 將龜裂白膠漿，透明漿，色漿，固化劑攪拌均勻印2-3次（每次刮3-4刀）

3. 自然干燥爆裂（要在臺(tái)板上面自然爆裂，要使用粘性好的臺(tái)板膠，靠張力去自然爆裂的）

4. 起布（必須完全爆裂后才能起布，因?yàn)槠鸩己蟛粫?huì)再自然爆裂）

注意事項(xiàng)

1. 龜裂漿一定要配打底透明漿使用，否則易脫落且沒(méi)有彈力；

2. 若膠漿印前太稠可加水，切勿加固漿以免影響爆裂效果；

3. 建議曬厚網(wǎng)印龜裂漿,一次印夠色為最佳.若用薄網(wǎng)印刷,請(qǐng)用冷風(fēng)吹漿層的表面,在漿層還沒(méi)有裂開(kāi)之前返印；(裂紋的大小與多少可以在龜裂白和龜裂透明的互配比例和印出來(lái)的漿層厚薄控制,龜裂透明比例越多和印出來(lái)的漿層越薄它的裂紋就越細(xì),反之它的裂紋越粗。

4.起布之后建議過(guò)熱壓燙一下，防止翹邊。